Baked Brass Alaska, or Arizona, or Albania?


After cleaning, some have suggested using the family oven but others have objected it may shorten the lifetime of the brass.

I wondered.

"... for brass that will be shot, cleaned and reloaded many times, after cleaning and rinsing it with water to remove any final dust/residue, does it shorten the lifetime of the brass to stick it in the oven to dry at some low (200F) temperature?
"Your comments, as a manufacturer of ammunition brass, would be most appreciated."

Now I’m sure that, with the shortage of reloading components right now, the recipients of these emails are all working 24/7 to catch up on the backlog so I wasn’t surprised that several couldn’t take the time to answer.

But three did, two of whom I will classify in the “expert” category. Here’s what they said.

"We do not manufacture brass.

"That said and done, we DO send all our brass to Cleve Black Oxide to turn it black. At our request, they will put it in  their ovens to dry it before we take it back.......no ill effects as far as we can tell.  150 - 200 degrees is not very significant as far as we can tell."
"Sticking your brass in the oven at 200° will not cause any harm to your brass. Heat won’t start affecting the brass until over 450° (actually more like 475°)."
"The melting and annealing temperature of brass is between 1700 and 1800 degrees depending on the exact alloy compound. Drying the brass at just about the boiling point should not effect the cases. They reach a much higher temperature at the point of ignition than this. They will only be exposed to this heat for a very short time since the water will evaporate quickly anyway."

Probably half of my brass is Starline and a good portion of what’s left is Remington. As manufacturers, they make top-quality products. I think that makes them experts. And from what I’ve seen and read, Crossfire seems to be right up there, too: They all say it’s OK.

So from now on, when the weather is not conducive to drying outdoors, I’ll turn the oven on to 200 degrees, cover a cookie sheet with aluminum foil and pour on the brass.

Baked brass, anyone?

Addendum

I’ve switched from dry vibratory cleaning (that needed a rinse afterwards to remove dust) to wet tumbling with stainless steel media (complete package from StainlessTumblingMedia.com). As the experts above report and I can confirm from my own experience with well-used and many-times-reloaded 45 ACP brass, there are no detrimental effects from the oven treatment at these low temperatures.

Addendum 09/03/2015

Here’s a useful quote - “Changes start to occur in brass grain structure at 480 degrees fahrenheit. To properly anneal brass, the temperature needs to be at 650 degrees F. for several minutes-BUT this will transfer too-much heat to the lower case in that time. So we need more heat for a shorter time. We need to raise the neck temp to about 750 degrees F. only for a few seconds to anneal.” See http://www.annealingmachines.com/how-to-anneal.html This would seem to indicate that 250 fahrenheit would be a safe temperature for drying. It’s above the boiling point so the drying should be quick, but more than 200 degrees below the point at which “changes start to occur in brass grain structure”.

History

EDSkinner.net began in 2023. Fiction and non-fiction publications are included as well as (blog) posts and supplemental materials from flat5.net (2004-present).

Comments submitted on individual pages are subject to approval. General suggestions may be sent via the Contact page.

© Copyright 2024 by E D Skinner, All rights reserved